Product details
Acrylic Resins For Wood Coating
Product |
Polymer Type |
Application |
Solid |
Tg(°C) |
Features |
WA-633 |
Pure acrylic |
Wood coating top coat |
41±1 |
35 |
Excellent transparency Fast drying Good resistance |
WA-631 |
Styrene acrylic |
MDF sealer |
46±1 |
45 |
Fast drying Good sand-ability Good resistance to "wood-grain bulge" |
YC-8410 |
Pure acrylic |
Wood coating |
41±1 |
45 |
Low film formation temperature Fast hardness rising Good early compression resistance |
PU-617A |
PUD |
Wood coating |
36±2 |
25 |
Excellent adhesion Fast in drying Good sanding performance Good build and high gloss |
PU-618B |
PUD |
Wood coating |
39±1 |
50 |
Fast drying, high hardness, good initial pressure resistance Good build and high gloss Good touch and oily feel Good compatibility with waterborne acrylic resin |
PU-619 |
PUD |
Wood coating |
39±1 |
25 |
Excellent adhesion Good build and high gloss |
YC-8430 |
Pure acrylic |
Wood & metal coating |
45±1 |
50 |
Outstanding climate resistance Outstanding chemical and blush resistance Outstanding water resistance |
YinYang Resinfor Water-borne MDF Basecoat WA-631
Typical Physical Data：
Type--------------------Styrene-acrylic emulsion
Appearance--------------Very slightly yellowish liquid
Solid（wt%）-------------46±1%
PH, 25℃-----------------8-9
Viscosity，cps-------------500-800
MFT ---------------------About 14℃
(The above is typical data, not the standard, actual standard is subject to COA)
Main Properties：
● Fast drying
● Good sanding-ability
● Good tolerance with pigments/fillers
● Good resistance to "wood-grain bulge"
PH, 25℃-------------------------8-9
Viscosity，cps---------------------<500
Tg ------------------------------About 35℃
(The above is typical data, not the standard, actual standard is subject to COA)
WA-631 Formula Reference
Name |
% |
White Pigment Paste* |
52.2 |
WA-631 |
40.0 |
AMP-95 Neutral Agent |
0.1 |
Water |
4.8 |
DPnB Film Forming Agent |
2.0 |
Deformer |
0.1 |
Wetting Agent |
0.3 |
PU Thickener |
0.5 |
White Pigment Paste Reference *
Name |
g |
Water |
20 |
Dispersion Agent |
1.0 |
Deformer |
0.2 |
Titanium |
56 |
Talc |
22.8 |
Total |
100 |
* 30-40 minutes dispersing at 1500RPM
YINYANG RESIN For High Transparent Water-borne Wood Coating WA-633
Typical Physical Data：
Type----------------------------Pure acrylic emulsion
Appearance----------------------Translucent liquid
Solids（wt%）---------------------41±1%
PH, 25℃-------------------------8-9
Viscosity，cps---------------------<500
Tg ------------------------------About 35℃
(The above is typical data, not the standard, actual standard is subject to COA)
Features：
● Excellent transparency
● Fast drying
● Good substrate wetting
● Good resistance to alcohol and so on.
YINYANG Synthetic Resin YC-8410
Product Description
YC-8410 is a core-shell structure, self-crosslinking pure acrylic emulsion. Its film forming temperature is low, fast drying, fast hardness rising, good sanding, good film transparency, high gloss, good hand feel, it has good alkali resistance and early compression resistance, suitable for water-based wood varnish and color paint. Alternative of DSM XK-12
Product Features
● Low film formation temperature
● Fast hardness rising
● Good early compression resistance
Resin Parameters:
Solid Content，% |
40-42 |
Viscosity， Cps |
0-500 |
Ph Value |
7-9 |
TG |
45 |
MFFT（℃） |
8 |
Film Property
Tack Free Time |
10min |
Pencil Hardness |
1-2H |
Gloss |
87 |
Adhesion |
0 |
Sanding Property |
excellent |
Water Resistance |
24h no whitening |
Early Anti-pressure |
excellent |
Alkali Resistance（10%） |
1h no change |
Alcohol Resistance（50%） |
1h no change |
(The above is typical data, not the standard, actual standard is subject to COA)
YINYANG DUAL RESIN for wood and metal coating YC-8430
(For wood and metal dual coating)
YINYANG Emulsion Latex YC-8430 is hydrophobic latex with ultra-small particle size, and
capable of ambient self-cross linking. It is designed to applied in transparency sealers,
outstanding durability coating on wood, masonry, and cement. It can also be used for floor
coating or carpark floor coating. This polymer has outstanding chemical, hot tire pickup and
blush resistance.
YC-8430 offers outstanding water and blush resistance. The ultra-small particle size allows
the latex to penetrate substrate surface, imparting excellent sealing properties. Gaining
from the property of ambient-cured self-cross linking, this product has excellent inherent
chemical and block resistance. YS-8430 offers the formulator wide formulating latitude,
requiring minimum quantities of additive ingredients for outstanding water resistance.
Performance Characteristics
● Ambient self-cross linking
● Hydrophobic latex
● Ultra-small particle size
● Outstanding climate resistance
● Outstanding chemical and blush resistance
● Outstanding water resistance
Typical Physical Properties
Appearance ………………………………………………. White, milky liquid
Total Solids, % by weight………………………………... 45.0±1.0
Viscosity 25°C, cps (Brookfield, LVT #3, 60, rpm) ……. <500
Density (Gram / milliliter)………………………………… 1.04
PH Value …………………………………………………. 7.0-9.0
Particle size, micron ………………..………………….. 0.07-0.10
Ionic ……………………………………………………….. Anionic
TG,°C ……. ……………………………………………… 50
MFT, 50% R.H., °C………………………………………. 45
(The above is typical data, not the standard, actual standard is subject to COA)
http://www.yinyangpolymers.com/